Tank Farm Design Recommendations for Corrosion Prevention

Tank Farm Design RecommendationsWhether designing a few above ground storage tanks or performing tank farm design for an entire facility, proper consideration should be given to the adverse impact of corrosion that can occur on the tank bottoms. When addressing the issue of tank bottom corrosion, consider the environment, the tank size and design, and the type of tank foundation to be employed. There are definite advantages in certain materials based on the size and requirements of an above ground storage tank (AST) foundation. By carefully assessing the tank farm surroundings and long-term requirements, costly and potentially dangerous corrosion related tank failures can be avoided. Whether you are relying on a reputable company in the industry or taking on your own front-end engineering and design, there are across-the-board tank farm design recommendations to consider when it comes to corrosion prevention:

In terms of corrosion prevention for under ground storage tank (AST) foundations, is cathodic protection (CP) effective?

For tanks erected on compacted soil or sand foundations, with or without a concrete ring wall, cathodic protection is considered a “good engineering practice” and has been proven as an effective means of addressing tank bottom corrosion concerns. When you compare various methods of corrosion prevention for above ground storage tank bottoms, CP is shown to prevail over asphalt or concrete unless your project involves smaller diameter tanks. The corrosion failure rate is greater for tanks built on asphalt or concrete compared to tanks where a concentric ring cathodic protection system is installed.

In terms of corrosion, when is asphalt or oil/sand acceptable for above ground storage tank (AST) foundations?

Asphalt foundations are not common in the United States, as the mechanical integrity of asphalt can be an issue depending on the AST environment. As well, the use of oil/sand layer designs has been phased out by most tank owners in the United States due to the adverse impact that these oil/sand layers have on cathodic protection systems. While historically prevalent in the Middle East and Asia, most larger national oil companies have abandoned this approach because it causes shielding of cathodic protection (CP) current, allowing corrosion to occur. Kuwait Oil, Aramco, and others now prefer clean sand combined with CP as the base material of choice. This is standard in the United States and has been for several decades.

What is a Concentric Ring Cathodic Protection System for above ground storage tanks (AST)?  

A. Designed for long-term storage, an AST cathodic protection ring system offers a factory-assembled design whereby the anode rings are ready to install with cable leads that extend past ring wall penetration. Concentric rings sizes are made to order, requiring no onsite welding, cutting, or splicing. The anode locations are marked, rings are laid out, and cabling is placed using a proven labeling system for future monitoring. A mixed metal oxide (MMO) anode is centered among a low-oxygen-generating coke backfill to eliminate depolarization.

Learn about MATCOR’s complete AST cathodic protection design services.

Are there some cases where concrete foundations are advantageous for tank farm corrosion prevention?

During installation of above-ground storage tanks, there are some advantages to concrete foundations for tanks when it comes to corrosion—the high pH of the concrete acts to passivate the steel, unless you have an above ground storage tank (AST) liner pad or something that is between the concrete and the tank bottom. If you can effectively seal the chime from the ingress of water and oxygen, the corrosion rates are generally quite small. Unfortunately concrete foundations for larger diameter tanks are not typically practical and can be quite expensive to properly install. Concrete foundations with appropriate AST liners are best for smaller diameter tanks.

In tank farm design for corrosion prevention, what are the best recommendations for above ground storage tank (AST) liners?

Plastic secondary containment liners are largely phased out in the United States and have been replaced by geotextile membranes that serve the same secondary containment purpose as plastic—they are conductive to allow cathodic protection (CP). The general standard in the United States is to have a CP system directly under the tank in order to minimize stray current or current losses due to earthing systems around the tank. Since the tank bottom is a large bare structure and the anodes are closely coupled to the tank bottom, there is usually very little current drain to other structures; the system if properly designed can accommodate modest current drain. While a plastic liner provides isolation from other nearby structures, when a problem arises with the CP system or if the CP system reaches the end of its projected service life, there is no way to install a new CP system without replacing the tank bottom.

Tank farm corrosion prevention is more manageable now than ever before. The MATCOR Concentric Ring Cathodic Protection System™ is just one of many excellent options for protecting your above ground storage tank (AST) from damaging corrosion.

For assistance with tank farm design, our Concentric Ring AST Cathodic Protection System™, project management or installation, please CONTACT US.

Learn more about Tank Cathodic Protection

Cathodic Protection Trends | Above Ground Storage Tanks

This presentation explores current cathodic protection trends for above ground storage tanks.

Statistics show owners of above ground tanks often experience external corrosion issues because of limited or poor installation methods. Typical above ground storage tank (AST) methods of the past involve a ring wall foundation that is generally formed with a sand or soil base, or even concrete for smaller tanks. It has previously been acceptable to use a galvanic ribbon anode system (generally magnesium), but this system often fails prematurely due to unstable sand-based foundations and poor connections. For this reason, the industry is moving away from the galvanic anode system and to newer concentric ring cathodic protection systems for above ground storage tanks.

Good Engineering Practices

While there are newer designs for AST cathodic protection systems, your first consideration should always be good engineering practices. The proper installation of a high-end AST cathodic protection system begins with known design specifications based on the tank size and diameter. This presentation compares traditional grid anode systems with newer linear anode concentric ring systems for the cathodic protection of above ground storage tank bottoms. In addition, congested terminal environments often lead to interference and less current at the tank bottom.

Grid Anode vs. Concentric Ring Cathodic Protection Systems

While the field-fabricated and field installed grid anode system has been in use for over 20 years, some faults have been discovered. Field installation presents welding challenges for the contractor because the system must first be secured, and it cannot be installed directly over sheet liner. The ribbon anode and titanium conductor bars have to be field cut to the appropriate lengths. At the conductor bar to anode ribbon intersections, a weld is applied. The field assembled grid system is subject to weld failures, the spot welds can be damaged easily during subsequent sand installation, and care must be taken to hold the system in place so that it does not short to the tank bottom. All of these installation challenges can adversely impact the system performance. Additionally, bare MMO in sand is an oxygen generator when used for cathodic protection. Oxygen is a depolarizer and in some instances this can lead to issues with maintaining polarization criteria.

Advantages of the Concentric Ring System

In comparison, newer concentric ring systems for above ground storage tanks include factory assembled anode rings that come equipped with the appropriate cable leads to extend past the ring wall penetration. No onsite field assembly is required. The system is pre-assembled in concentric ring sizes designed for your tank and requires no cutting, splicing, or welding, and the MMO wire is backfilled within a braided fabric sleeve with coke breeze. Anode locations are simply marked, each ring is laid out at the proper diameter, and cabling is extended toward the ring wall. The anode cables are labeled for ease of identification and to allow for monitoring of current to each anode ring. Unlike the grid system, the MMO anode is centered in a coke backfill – this coke environment inhibits the generation of oxygen eliminating the issues with depolarization.

The concentric ring tank cathodic protection system is designed for longevity. A typical under-tank ring system using MMO anodes exceeds a 30-year life, however can be designed to extend life beyond 100 years.

Additional Considerations for Tank CP

  • Some tank operators opt for a “replaceable” anode system, however time and manpower are required to extract and replace the anodes and backfill and the design life is only 30 years.
  • Volatile corrosion inhibitors (VCI) are often used in conjunction with cathodic protection systems where CP cannot be installed or may be ineffective, such as ring wall crevices, poor bottom-to-sand contact, and more. It can be pumped under tanks via shielding high-density polyethylene (HDPE) containment liners.

Today, tank owners have more effective choices than traditional grid anode systems for tank cathodic protection. The MATCOR Tank Ring Anode™ System is trending as a high-end solution for above ground storage (AST) tanks.

For assistance with tank cathodic protection system design, MATCOR’s Tank Ring Anode System, project management or installation, please CONTACT US.

Learn more about AST Cathodic Protection

April 24 is Corrosion Awareness Day

Did you know that corrosion costs us an astounding 2.5 trillion dollars globally?

Not to mention corrosion can cost lives and jobs…

Today is corrosion awareness day, so we thought it would be a good idea to reiterate the importance of the NACE IMPACT (International Measures of Prevention, Application, and Economics of Corrosion Technologies) study released in 2016.

According to the study, most corrosion failures, and nearly all catastrophic corrosion failures are preventable. And nearly $875 billion can be saved through the right prevention and risk analysis efforts.

Through the IMPACT study, NACE determined that in order to reduce the astronomical cost of corrosion, we would have to change how decisions are made regarding corrosion. We must not only continue to develop corrosion control methods and technology, but we must utilize organizational management systems and risk tools throughout all levels of an organization to achieve the greatest success in saving lives, jobs and money.

You can learn more by visiting

Impressed Current Anode Systems for Jetty Piling

One of the key decisions for any cathodic protection system design is the choice between an impressed current anode system or a galvanic (or sacrificial) anode system. This is especially true for marine applications where cathodic protection is commonly applied to structures such as steel piling systems on jetties and piers for corrosion protection. A recent MATCOR project highlights the choice between ICCP and Galvanic systems on a newly constructed jetty in Surabaya, Indonesia.

Impressed Current Anode Systems vs Galvanic Anode Systems

impressed current anode systems for jetty piling
Click on the image above to read the full case study comparing impressed current cathodic protection utilizing marine anode sleds with a galvanic anode system.

This case study article, which appeared in the October issue of Materials Performance includes a comparison of key factors for commonly used galvanic (aluminum) anodes and impressed current (titanium with mixed metal oxide) anodes. The key differences between an impressed current anode system and a galvanic anode systems include:

  • Anode consumption rates
  • Current density (CD) limits
  • Driving voltage
  • Anode quantities
  • Installation time and costs

The article describes these key differences in more detail.

Conceptual Design – Galvanic vs Impressed Current

Jetty applications can be designed using either galvanic anodes or impressed current anodes, and often it is a matter of client or designer preference. For this project in Indonesia, the cathodic protection designer reviewed both system types to determine the ideal design for this application based on a 30-year anode life. The final decision was based on several factors including total number of anodes and installation time required, in addition to safety considerations.

Impressed Current Anode System Installation and Commissioning

The final design called for the installation of six marine anode sleds, which took less than a week to complete.

For more details about this impressed current anode system solution for jetty piling cathodic protection, please read the full article in the October issue of Materials Performance. You can also access the full article HERE.

For assistance with impressed current anode system design, MATCOR’s Sea-Bottom Marine Anode Sleds, project management or installation, please contact us at the link below.

Contact a Corrosion Expert

Best Cathodic Protection Paper and Excellence in Corrosion Science at CORCON 2016

We recently joined fellow Brand Energy company SGB Scaffolding and Industrial Services as Silver Sponsors of CORCON 2016. CORCON, held in September in Delhi, is NACE International Gateway India Section’s premiere event in India and NACE International’s 2nd largest conference.

Please join us in congratulating two of our colleagues recognized during CORCON:

Corrosion Awareness Award

Mr. Shailesh Javia, division head for SGB in India, was awarded the NIGIS Corrosion Awareness Award, presented to individuals and institutions for their contribution to corrosion awareness and developments in the field of corrosion science and technology in India.

Best Paper – Cathodic Protection Track

Mr. Ted Huck was awarded Best Paper in the cathodic protection track for his presentation entitled AC Interference Modeling And Mitigation Materials.

In addition to Mr. Huck’s award-winning paper, we presented four additional technical papers at CORCON:

  • Impressed Current Cathodic Protection of Internal Submerged Surfaces of Carbon Steel Water Storage Tanks, presented by Mr. Shailesh Javia, SGB and E. Gopal, MATCOR
  • Atmospheric Corrosion Inspection of Above Ground Piping, presented by Mr. Jeffrey L. Didas, MATCOR
  • Impressed Current Anode Systems for Jetty Piling Protection, presented by Mr. Shailesh Javia, SGB
  • Corrosion Prevention of Aging Pipelines with Deteriorated Coating by Application of Linear Anode ICCP System, presented by Mr. Ted Huck, MATCOR

To learn more about MATCOR’s cathodic protection systems and AC mitigation materials, please visit If you have questions or need assistance please complete our web form to connect with our corrosion experts.

To learn more about SGB, please visit

Dean Lioliou Joins MATCOR

MATCOR Houston, Dean LioliouWe are pleased to welcome Dean Lioliou to the MATCOR Team as the Gulf Coast Region Account Manager.

Dean was most recently over sales for ALS Oil & Gas’ Pipeline & Asset Integrity division. His focus was on fiber optic pipeline leak detection, cathodic protection monitoring, corrosion under insulation analysis through thermal imaging technology, and pipeline leak surveying utilizing drone technology. Prior to ALS, he spent many years at Abriox as the Southern Area Regional Sales Manager focusing on Cathodic Protection monitoring.

Dean is very involved with NACE, currently serving as Vice Chairman of the TX/LA Section, a member of the exhibits and conferences committee for NACE International, and is involved in the Houston, San Antonio, and Corpus Christi sections. He is also NACE CP Level 2 certified.

Please join us in congratulating Dean and welcoming him to the organization. He can be reached at 832-755-2714 or by email at

Canister Anodes: HSCI vs MMO

Canister anodes are commonly used for impressed current anode cathodic protection applications. These can be used to protect buried metallic piping in congested plant environments, to protect distribution or transmission pipelines in either distributed shallow ground beds or as horizontal remote ground bed anodes, and to protect other structures such as above ground or buried tanks and piling systems.

mmo-canister-anode-emailMATCOR’s MMP™ Anode provides an outstanding combination of value, quality and proven reliability for use with these types of applications and are often a direct upgrade over other canister anode offerings. Below is a comparison of MATCOR’s MMO canister anode vs. conventional high silicon cast iron anodes, in addition to a real life project example comparing the costs associated with both canister anode types.

MMP Canister Anode Unique Construction Features

Understanding the value of the MATCOR MMP™ anode product, starts with its unique construction features as follows:

HSCI vs MMO/Ti Canister Anode Type

Most canister anodes consist of either a High Silicon Cast Iron (HSCI) anode or some configuration of MMO/Ti anode installed in a large metallic “canister” that is filled with coke backfill. The canister is capped with the anode cable extending out the top of the anode cap. Once installed, the exterior metallic canister housing is part of the anode system and will consume quickly as current is discharged off the anode, through the coke backfill and then off the external metallic housing.

It is important to note that the housing is only intended to survive transportation and installation. Once installed, it is expected to be consumed, leaving behind the anode and coke backfill.

One of the most important considerations in evaluating any canister anode technology is to evaluate the anode technology that is inside the canister anode.

HSCI anode technology is an older anode technology that remains extremely popular around the world. It is popular because it is cheap and readily available from many suppliers. Because HSCI anodes are simply castings of a specific formulation of iron, they are available from a wide range of manufacturers with casting facilities spread across the globe. Any foundry can cast the basic HSCI anode. Testing for anode composition assures that the basic elements are present in the correct ratio, however, the mechanical and more importantly the electrical (anode) characteristics are dependent on a lot more than just having the correct ratio of components. Also critical are the canister anode:

  • Casting process
  • Micro-structure
  • Density and consistency of the casting
  • Presence of trace elements
  • Consistency of the grain structure
  • and more…

Unfortunately, it is very difficult to assess the quality of a particular anode casting batch without extensive long term testing. Even the most experienced and reputable cast iron anode suppliers will admit that HSCI anode quality and anode performance can vary significantly even within different casing batches from the same manufacturer.

This leaves buyers with a real challenge in confirming that the anodes they are purchasing will provide the anode life and current output that they are specifying because of the wide range of casting quality issues that can occur with HSCI anodes and the large number of casting facilities offering this type of product.

Mixed metal oxide coated titanium (MMO/Ti) anodes are also a common anode technology utilized in canister anodes – typically these anodes consist of a titanium substrate on to which a mixture of mixed metal oxides is electro-deposited on to the substrate and thermally cured. The MMO coating typically uses a base of Iridium as the primary catalyst that allows the coating to perform as an anode.

MMO Anodes Easier to Test for Quality

As with HSCI anodes, quality is an issue with MMO/Ti anodes; however, there are some key factors that lead to making MMO/TI anodes easier to QA/QC than conventional cast iron anodes.

First, there are no real mechanical concerns other than assuring that there is good adherence between the MMO coating and the underlying substrate. Because the substrate is pure titanium the mechanical properties are quite consistent (ASTM Grade 1 or Grade 2 Titanium is considered commercial pure titanium and either can be used for MMO/TI anodes). Testing for coating adhesion is a rather simple test that can be performed on a test coupon from the same process or on the anode itself.

In addition to having a very stable, homogeneous substrate, the MMO/Ti anode performance can be tested using accelerated life testing to provide an evaluation of the performance of the specific coating mixture that is applied. As with HSCI anodes, there are a large (and growing) number of suppliers of MMO/Ti anode materials; however, testing can be used to confirm the anode material quality. MATCOR MMP™anodes use MMO/Ti anode material with a proven track record. Additionally, third party inspection and testing of MATCOR’s MMO/Ti anode material is available for a nominal inspection charge.

Canister Anode Configuration

The actual anode inside the canister can have a wide range of configurations; however, the most common configuration is the tubular anode. All HSCI anodes are cast in tubular (either solid or hollow tubular) configurations and many of the MMO/Ti canister anodes also use tubular anodes.

For HSCI tubular anodes, the brittle nature of the anode must be taken into consideration when transporting, handling and installing the anode as dropping the anode canister can lead to breaking or cracking of the HSCI anode.

MATCOR’s MMP™ Anode is unique in that we utilize a solid titanium rod as our substrate. This provides several advantages over typical MMO/Ti configurations utilizing tubular anodes. The cable to anode connection is easier and more secure when connecting to a solid rod as opposed to trying to connect a cable to the inside of an anode tube. The solid titanium rod is also stronger and unlikely to break should it be bent.

Other MMO/Ti configurations can also be used inside a canister anode including MMO/Ti strips and ribbons. There is nothing inherently wrong with these configurations as long as the anode to cable connection is properly designed. Improper anode to cable connection designs can lead to premature anode failure.

Canister Anode Connection Technology

Typical anode connections used for discreet canister anodes usually consist of some version of a pressure fit mechanical connection with an epoxy sealant covering the anode to cable connection. Anode to cable connection failures have historically been a significant cause of premature anode failure. Depending on the anode type and configuration, the location of the anode connection can also have an impact on performance – especially for HSCI anodes that consume rapidly and may be subject to necking effects– with MMO/Ti anodes that are dimensionally stable (i.e. do not physically consume) this is much less of an issue.

MATCOR’s MMP™ anode utilizes a multi-step welded connection technology to assure the anode to cable connection is mechanically and electrically secure and properly sealed from the ingress of moisture that can lead to premature anode failure. The multi-step anode connection includes a mechanical crimp followed by a welding process. The mechanically secure welded connection then has a layer of non-conductive hot melt sealant followed by a heat shrink sleeve with a second sealant layer on the interior of the heat shrink. This heavily engineered connection technology has proven to be exceptionally effective with hundreds of thousands of connections in service over the past 20 years.

Typical spiral wound 0.7mm thin walled canister

Heavy Duty Canister Anode Construction

Most canister anodes are constructed using a thin walled galvanized steel spiral wound pipe material. This material is commonly used in the HVAC world as a ducting material and is readily available commercially. This material is typically 0.7mm thickness (24 gauge) with a spiral wound construction. This type of canister provides only a modest amount of mechanical strength and must be very carefully handled during transportation and installation.

MATCOR’s 1.85mm EMT seamless steel pipe offers 250% thicker wall

MATCOR’s MMP™ Canister anode utilizes a thicker walled EMT seamless steel pipe with a typical material thickness of 1.8 mm or 250% times the thickness of typical canister anodes. This additional wall thickness makes the MMP™ anode a much stronger product – you can drive a fork truck or backhoe over our anode and not significantly damage the canister.

Economic Considerations

The actual installed cost of the anodes is an important consideration in selecting the optimal anode solution. As noted previously, the anode system quality and design integrity should also be factored into the evaluation as these factors can serve to reduce the anode system’s life in the field.

Some factors that should be considered include:

Anode Operating Life (Amp-Years)

Every anode has an operating life. For HSCI anodes the calculation of an anode life is complicated by the inherent variability in HSCI anode casting. The nominal consumption rate of HSCI anodes is typically assumed to be between 0.5 to 1.0 lbs/amp-year (0.23 kg/amp-year to 0.45 kg/amp-year) in a coke backfill. This wide range is consistent with the variation in anode consistency and quality inherent in the anode type. The consumption rate can also vary depending on the environment and the operating current density.

Additionally, a utilization factor is typically applied to the calculations as the anode can never be fully utilized – at some point the anode consumption is such that the anode to cable connection is lost prior to fully consuming all of the anode’s mass. For stick anodes with an end connection this is typically 65% (meaning that 35% of the anode mass is unusable) while for tubular anodes with center connections this utilization factor is closer to 85%.

MMO/Ti anodes are considered dimensionally stable anodes and do not physically consume. They are instead electro-catalytic in nature – they cause a reaction to occur that generates DC current flow without actually being a reactant and thus are not consumed. The catalytic component in the MMO coating does; however, have a finite life that is relatively consistent and can be determined based on the accelerated testing performed by the manufacturer.

The challenge with MMO/Ti anodes is that the coating loading is on the order of mg/m2. With such a light coating load, it is often difficult for the anode manufacturer to control the coating loading to exactly the thickness that would be optimal. Most MMO/Ti anodes are supplied with more coating than required to assure that the coating thickness QA/QC spot checks exceed the minimum specified coating loading. MATCOR’s experience has been that the anode coatings tend to exceed that required coating loading by a significant margin assuring even longer life than the stated design life.

Anode Weight

One of the key advantages of the MATCOR MMP™ anode is the low weight over HSCI anodes for a similar current capacity. HSCI anodes consume at a relatively high rate and require significant anode mass to provide the current output and life required. Weight has two key impacts; one is economic as the lower the anode weight the cheaper it is to transport and install, and the second is a safety issue as the heavier the anode the greater the risk of injury associated with the proper transportation and handling of the anode during installation. While the transportation costs are easily quantified, the safety benefit of a much lighter anode to be installed is much more difficult to quantify but should be considered in the anode selection.

Anode Installation Replacement Cost

Another consideration that should be given is the cost of having to replace an anode installation more frequently. This metric is often not considered; however, there is a very real value to having an installation that lasts 25 years versus only 18 years and the additional incremental cost for the additional life has a real value that should be considered in the economic evaluation.

Savings from using fewer, higher output anodes

Another consideration that is often overlooked is the savings that might be achieved by using fewer anodes that are capable of higher output to reduce the overall installation costs. The incremental cost of fewer, larger anodes could result in a significant cost savings over using more anodes that are rated for lower output. When considering the use of fewer, higher output anodes the impact on system resistance could be an issue as the power supply may have to be larger and the operating power higher to overcome the additional system resistance from fewer anodes. Typically power costs are rather nominal and not a major consideration in this type of economic evaluation.

Canister Anodes System Example

Please note that this is a real project example and is intended to show the methodology used to evaluate two different options – one using HSCI anodes and the other using MMP™ canister anodes. The costs associated with this project are not suitable for other applications – each project has its own costs that must be evaluated for that specific project.

Cathodic Protection Requirements

Shallow horizontal ground bed rated for 60 Amps using multiple anodes in parallel at a depth of 12 feet and spaced 15 feet from each other. Each hole would be 8” diameter and the hole would be filled with coke around the anode including one foot below the anode and one foot above the anode. System to be suitable for 30 years anode life. Soil resistivity is assumed to be 3000 ohm-cm.

Canister Anode Options

Two anode options were considered as follows:

 HSCI Solid Stick AnodeMATCOR MMP™3605
Anode TypeBare HSCI AnodeCanister MMO/Ti rod
Anode Dimensions3" x 60"3" x 60"
Anode Weight, ea110 lbs44 lbs
Anode Life, ea95.3 amp-years*125 amp-years
Anode Cost$325$210
Freight Cost/Anode$22$9
* Based on 0.75 lbs/amp year consumption rate and 65% utilization factor for solid stick anode

Additional Costs

  • Installation cost to drill each hole, install anode and make header cable connection estimated at $700 USD/hole
  • 180 lbs of coke backfill per hole, including freight, estimated at $135/hole
  • Cable costs for header cable, estimated at $1 per foot
  • Cable to anode splice kit estimated at $35 per connection


Minimum number of anodes required to meet 30 year life operating at 60 amps:

Roundup {(60 amps x 30 years) / Anode life} = minimum # of anodes

  • HSCI Stick Anode – 19 anodes resulting in 30.19 years design life
  • MATCOR MMP™ – 15 anodes resulting in 31.25 years design life

Anode System Resistance

Based on Dwight’s equation using an 8” diameter hole and 7 ft coke column in 3000 ohm-cm soil the resistance of a single anode (Ra) is 7.68 ohms. The resistance for multiple anodes in parallel is Ra/Number of parallel anodes

  • 19 HSCI anodes – anode bed resistance is 0.40 ohms
  • 15 MMP™3605 anodes – anode bed resistance is 0.51 ohms

Installed Cost

Based on the cost assumptions the total installed costs are:

  • HSCI 19 anode system:    $23,408.00
  • MATCOR MMP™ 3605:    $16,560.00

Contact MATCOR about your canister anode cathodic protection requirements or learn more about our MMP Anode (MMO) canister anodes.

MMO Anode Technology: The latest in Cathodic Protection

MMO anode technology has taken over the cathodic protection industry and MATCOR has been on the forefront for the last 20 years. Ted Huck, our VP of International Sales was interviewed at the recent NACE Corrosion Conference. In this video he discusses MMO anode technology for cathodic protection systems and the importance of reliable anode to cable connections.

MMO Anode Technology

MMO anodes, or mixed metal oxide anodes are the latest technology in the corrosion industry. Mixed metal oxide anodes are lightweight and durable with a very low consumption rate. 

MMO anodes are a mix of metal oxide electrocatalysts. In the presence of a DC voltage source they cause an electrical reaction that generates cathodic protection current. Unlike conventional impressed current anodes that physically consume as part of the cathodic protection reaction (at rates measured in kg/amp-year), MMO anodes are dimensionally stable and do not consume. Instead, they have a long and predictable catalytic life. MMO anodes consist of a thin coating of the MMO catalyst over an inert lightweight titanium substrate and are available in a wide range of shapes and configurations.

Why Cathodic Protection Systems Fail

Waterproof Anode to Cable Connection to protects MMO anode cathodic protection systems
Kynex® Patented, Waterproof Anode to Cable Connection

The most critical component to any cathodic protection anode system is the connection of the anode to the cable that runs back to the power supply. Because the cable is part of the anode system, if it has any nicks or defects or is not water tight, that cable can become part of the anode and will very quickly consume. When that happens, the anode fails. So, with cathodic protection systems it is imperative to have the highest quality connections.

Typically, when a cathodic protection anode system fails, it is not the anode that fails, it is the anode connection that fails. MATCOR has developed a proprietary technology for connecting wire anodes to cable, called Kynex®. Wire anodes are the heart of a lot of our products and this proprietary anode technology is a huge leap forward in the reliability of these connections.

Cost-effective, Reliable Cathodic Protection Solutions

At the end of the day, for our clients, it’s all about delivering value. It’s providing a cost effective solution that’s going to serve them for a very long time. As a designer and manufacturer of cathodic protection anode systems, we are able to specifically address client needs with customized corrosion prevention solutions that provide:

  • Long life
  • Great economic value
  • Superior reliability

MATCOR Products and Services

MATCOR is one of the world’s leading cathodic protection companies. We design, manufacture, install and service cathodic protection systems for clients worldwide. MATCOR provides services to the pipeline, midstream and oil & gas industries, protecting assets such as pipelines, storage tanks, and compressor stations. We also do a lot of work in the power industries, petrochemical, and chemical industries. Anywhere where you have buried steel structures, we are there to stop corrosion.
We encourage you to contact MATCOR through our website where our corrosion specialists and engineers can provide a solution tailored to your needs.

Video Demonstrates Cathodic Protection System Installation

Iron Gopher® Impressed Current Linear Anode System designed for horizontal directional drilling (HDD) is installed beneath an above ground storage tank (AST)

Chalfont, PA (May 27, 2015) – MATCOR, Inc. the trusted full-service provider of proprietary cathodic protection products, systems, and corrosion engineering solutions recently released a video showing the installation of the company’s Iron Gopher impressed current linear anode system at the site of an above ground storage tank in Texas.

Trenching to install cathodic protection systems may not be feasible for applications such as cross country pipelines, congested industrial environments and under above ground storage tanks. For these horizontal directional drilling applications, a linear anode with superior mechanical strength is required. The Iron Gopher with Kynex® technology is the only impressed current linear anode designed specifically for cathodic protection in horizontal directional drilling applications.

“As another example, Colonial Pipeline installed several thousand feet of our Iron Gopher® linear anode at an HDD project in NE Georgia,” said Ted Huck, VP of Sales for MATCOR. “With its unique design and greatly increased strength, Iron Gopher is superior to anything seen in the market for cathodic protection in HDD applications.”

Learn about MATCOR’s complete cathodic protection installation services.


Locally, MATCOR’s Emphasis is on Giving Back

As a full service provider of cathodic protection systems and corrosion engineering services to the oil and gas, power, water/wastewater and other infrastructure industries, MATCOR is well known worldwide.

When it comes to the local business community however, our closest customer is about 50 miles away. In Bucks County, Pennsylvania, where we’re headquartered, we like to give back and encourage employees to get involved with local nonprofits.

Heather Davis, MATCOR Human Resource; William Schutt, MATCOR Chairman; Dana Baedke; President of Key Marketing

“I think it’s just what we have to do,” said Bill Schutt, who founded MATCOR forty years ago. “If we can give organizations not just money, but time and advice, it could be a huge, huge help.”

Mr. Schutt, along with MATCOR marketing consultant Dana Baedke and employee Heather Davis sat down recently with The Bucks County Herald to talk about giving back and how it comes full circle.

Ms. Baedke met Mr. Schutt five years ago through a local nonprofit, the Women’s Business Forum, where he served as her mentor. Baedke is now giving back as president of the organization and owns a successful marketing business, Key Marketing, with MATCOR as a client. Ms. Davis has become involved in another local nonprofit, Network of Victim Assistance (NOVA), where she has served on the young advisory board and helped to organize the 2nd annual No Bullying Run, where MATCOR was a sponsor. These are just a few examples of the organizations and people touched by our employee’s local efforts.

“As a company,” Schutt said, “we started giving money and time, and what’s happened, which just blows my mind, is almost every week there is some sort of drawing, event or something for local charity I have nothing to do with. The folks here at MATCOR do it on their own.”

Read the full article in the Bucks County Herald.